Sensitivity setting for ultrasonic testing as per ISO 17640

 

Range and Sensitivity Setting  for Ultrasonic testing

Setting of range and sensitivity shall be carried out prior to each testing in according to this procedure. The temperature difference between the time of range and sensitivity setting and time of test should be within ± 15°C.



Checks to confirm these settings shall be performed at least 44 hour once and on completion of tests.

The checks should also be done whenever a system parameter is changed.

If deviations are found during these checks , corrections given in the below Table. 1 shall be carried out.

Ultrasonic testing

Reference for Sensitivity Setting for Ultrasonic Testing

One of the following technique shall be used for setting of reference

Technique 1: The reference is a Distance Amplitude Curve (DAC) from a dia 3mm side drilled hole.

UT testing reference

Technique 2: The references for transverse and longitudinal waves using the distance gain size technique (DGS) based on the diameter of the disk shaped reflector (DSR) are given in the table 2 & Table 3.

UT Testing reference levels

 

Technique 3 : The Reference notch shall be 1mm wide, rectangular with depth of 1mm . This technique applies only for thickness range 8mm  u t<15mm and fr beam angles W 70°.

UT Testing techniques

 

Technique 4 : For the tandem technique, the reference is a flat bottom hole of 6mm diameter (for all thickness), perpendicular to scanning surface. This technique is applicable only beam angle 45° and thickness  tW 15mm .

The length of the side drilled hole and notches shall be greater than the width of the sound beam measured  at -20 dB  .

Transfer Correction

When separate reference block is used for establishing reference levels, a measurement be made for transfer differences.

Step 1 : Set the echo reflected from a corner of the reference block at 80% of full screen height . The decibal dB required for the setting is noted,  Db reference.

Step 2 : Set the echo reflected from a corner of the test  weld material at 80% of full screen height . The decibal dB required for the setting is noted , Db Test.

Step 3 : The Difference between two values , Db reference – Db Test = Transfer Correction.

  • If the difference is less than 2dB, then the correction is not required.
  • If the difference is more than 2dB and less thaan 12 dB, then the compensation is given to the machine.
  • If the transfer loss exceeds 12dB , the reason shall be considered and further preparation of the scanning surfaces shall be carried out , if applicable.
  • When there is no apparent reasons for high correction values, the attenuation  at various locations on the test object shall be measured and where it is found to vary significantly, corrective actions shall be considered.

Sound to Noise ratio

During testing of weld, the noise level, excluding spurious surface indications, shall remain at least 12 dB below the evaluation level . This requirement may be relaxed subject to specification.

For more detail of Ultrasonic testing services and other NDT services feel free to contact us at https://aqcinspection.com/ for best services.

Visit our technical and career updates at our Blog site https://advancedqualitycentre.blogspot.com . https://ndtcenter.blogspot.com our website https://aqcinspection.com/news-events/  for many more blogs

Location: 116-B, 5th St Ext, 5th Street Extension, Gandhipuram, Tamil Nadu 641012, India

Comments

  1. Eiwaa GroupsMarch 17, 2021 at 2:36 AM

    Thanks for this post. Service Provider of Eddy Current Testing in UAE Service offered by EIWAA Group, Sharjah, UAE. Eddy Current Testing in UAE
    Water Bag Rental Services

    ReplyDelete

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more