Welding with filler wire- procedure

 

Welding is a process of joining two base metals by heating it. It can be done with or without additional filler metal being used.
Below are the few types of welding process :
1)Shield Metal Arc Welding,
2) Metal Inert Gas Welding
3) Tungsten Inert Gas Welding
4) Oxygen fuel gas welding
5) Friction Stir Welding (no filler metal required)
6) Electric Resistance Welding (no filler metal required)
and few more….

Gas welding procedure

For welding with additional filler wires, care should be taken that the selected filler wire or electrode is compatible for the metal being joined.

Collect the Material Test Certificate of the material . Batch test certificate of the filler wire and verify the values.

First step is to check the chemical composition of filler wire. The minimum required chemical content should be present and maximum allowed chemicals should be restricted in the filler wire. If Carbon Equivalent value is restricted for the base metal then check the carbon equivalent value of the filler metal. Verify the value is maintained in the required level.

Second is to verify the Tensile strength of the selected filler wire material. The Tensile strength of the filler wire should be equal to or more than the Tensile strength of the material being joined. Being the materials joined are similar metals.

Third step is to verify the filler wire or electrode satisfies additional requirements such as low hydrogen content, impact toughness property,low temperature or elevated temperature toughness property, high temperature elongation property, Hardness values. If the base material to be joined are having those property then the filler wire electrode selected should posses those properties.

Finally the selection of size of filler wire or filler wire formed can be made as per the welding process. Thickness of the welded metal, root gap possibly present and amount of metal to be filled in a single pass.

An procedure qualification test shall be done with the selected filler metal on the sample test specimen. With a thickness in between the range of thickness to be welded. Care should be taken that the welding paremeters such as Current, Voltage, Welding Travel Speed, Heat Input value (kJ), Weld bead width, Weld metal thickness are all maintained at allowable limits. These limits are derived from previous experiences and practices said in standards.

Welding procedure

After the test Weld has been made, it is non destructive tested for defects and accepted Weld specimen is cut and tested for its mechanical properties.
All tests required to prove it’s required properties are done, before approving any welding process.

To qualify only the Welding electrode or filler wire,  Tensile Test and all Weld mechanical tests are done. The sample for testing is cut only from the Weld metal, i.e longitudinally in the Weld.
To qualify the whole welding procedure the mechanical test samples are cut in transverse to the Weld seam.

For more guidance to your welding process and more to qualify a welding procedure or selection of weld samples, welding failure analysis, welder qualification and Welder Certificate reach us at https://aqcinspection.com/

Also for non destructive testings NDT and mechanical testings for you PQR /WPS qualification, we have a dedicated facilities, to know more see https://aqcinspection.com/mechanical-testing-services/

Find our Blog updates from https://advancedqualitycentre.blogspot.com

Comments

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more