WELDING TEST COUPON PROCEDURES

 

Welding Procedures

Follow a clear example of  test coupons welding procedures for a 3G welding certification. In this 3G  welding procedure the notes were taken from the same section of the AWS code that are used for the 3/8 inch limited thickness test procedure.

weld test coupons

The test coupons shall be pre-cut and ready to prepare. The welder shall grind the face of the test plates a minimum of one inch back from the bevel and a minimum of a quarter of an inch.

Next the backing bar to bare metal shall be cleaned with a grinder and cleaned the oxidation off of the bevel, to bare metal. After the Welding Inspector will check the bevel angles with a protractor.

1. The Root Pass:

The welder shall set to root opening with two 1/8 inch welding electrodes and then the test plate shall be inspected for fit-up. The test coupon shall be put in a vertical position and marked with a white marker to make sure not move the plate anytime during welding or cleaning. This is done because the AWS procedure notes state:

“Now the test will be placed in the fixed position. The test piece will be marked in position with a marker and the Inspector may see the test anytime during  the testing. During the test, the pieces shall not be moved in any direction and or removed from the testing place without the Inspectors approval”.

root pass weld procedure

After the root, the welding procedure states:

“The root of the weld shall be inspected, and there shall be no evidence of cracks, incomplete fusion, or inadequate joint penetration.

A concave root surface is permitted within the limits shown below, providing the total weld thickness is equal to or greater than that of the base metal.

The maximum root surface concavity shall be 1/16 in. (1.6 mm) and a maximum melt-through shall be 1/8 in. (3 mm)”

2.  The Hot Pass:

The hot pass shall be done using the same technique as the root pass. A single pass shall be filled with no restarts. The slag shall be cleaned.

hot pass welding procedure

3.The Cap Weld:

The plate shall be let to cool down till the welder could almost touch it. The cap of the weld shall be done using the weave technique, while washing the weld about 1/16 of an inch past the edge of the bevel.

 

The sides must be held for about a second before moving back to the other side. The cap shall be also done in a single pass just like the root and hot pass. The welder must give good weld penetration, preventing face bend failure and undercut.

The acceptance criteria for the face of the weld are as follows, according to AWS:

“The face of the weld shall be flush with the surface of the base metal, and the weld shall merge smoothly with the base metal. Undercut shall not exceed 1/32 in. (1 mm). Weld reinforcement shall not exceed 1/8 in. (3 mm)” 

The first picture below is the weld still covered in slag. The second picture is the slag lifting itself off of the cap. The last picture is the cap cleaned with a wire brush.

cap welding

To be continued in the next blog…

we provide standard specifications for welding procedures for all welding process and Brazing. We offer Welder Procedure Specification, Welder Certificate Renewal Process, Procedure Qualification Record, Welder Qualification Testing, welder Training and Welder qualification services  in Coimbatore,Trichy, Salem, Erode, Chennai.

Please feel free to reach us https://aqcinspection.com/training/ to learn more about any of the methods in detail.

Visit our technical and career updates at our Blog site https://advancedqualitycentre.blogspot.com . or

https://ndtcenter.blogspot.com

Location: Advanced Quality Centre,116-B, 5th St Ext, near Kalyan Jewellers, 5th Street Extension, Doctor's Colony, Gandhipuram, Tamil Nadu 641012, India

Comments

  1. Jhon DavidApril 20, 2022 at 10:22 PM

    We Specialize In World-Class Welding School . Call Us Today To Get Started! Our Welding Classes Feature Hands-On Training And Vary From Beginner To
    Get your career started on the right path with welding training from Centura College. Start Your welding career training with Centura College in Richmond. Learn more! Day or Evening Schedules. Job Placement Assistance. Train In..

    ReplyDelete

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more