Levels of Certification AWS 1:2003

There are three levels of qualifications for welding inspector personnel. These levels are:


  1. AWI – Associate Welding Inspector;
  2. WI – Welding Inspector;
  3. SWI – Senior Welding Inspector.

welding inspector


1.1)      Associate Welding Inspector (AWI):

Shall be a high school graduate, or hold a state or military approved high school equivalency diploma. Shall have a minimum of two years’ experience in an occupational function with a direct relationship to weldments fabricated to national or international standards and directly involved in one or more of the areas.


1.2)      Welding Inspector (WI):

 Shall be a high school graduate, or hold a state or military approved high school equivalency diploma. Shall have a minimum of 5 years’ experience in an occupational function with a direct relationship to welded assemblies fabricated to national or international standards and be directly involved in one or more of the areas.


1.3)      Senior Welding Inspector (SWI):

 Shall be a high school graduate, or hold a state or military approved high school equivalency diploma. Shall have a minimum of 15 years’ experience in an occupational function with a direct relationship to welded assemblies fabricated to national or international standards and be directly involved in one or more of the areas.


Written Test Requirements.


Shall be performed an applicable AWI, WI, or SWI examination. Individuals failing one Part of the examination shall have to retest on all Parts. The examination includes the following Parts:

1) Test on the requirements of a code, standard or specification. A test on fundamental principles including, but not limited to: welding processes, NDT examination, safety, quality assurance, inspector’s duties, weld discontinuities, welding symbols, joint design, mechanical properties of metals, and basic on-the-job mathematics.

2) A test on practical application of welding inspection knowledge including, but not limited to: welding procedure qualification, welder qualification, mechanical testing, drawing and specification compliance, welding examination, and nondestructive testing processes.

we provide standard specifications for welding procedures for all welding process and Brazing. We offer Welder Procedure Specification, Welder Certificate Renewal Process, Procedure Qualification Record, Welder Qualification Testing, welder Training and Welder qualification services  in Coimbatore,Trichy, Salem, Erode, Chennai.

Please feel free to reach us https://aqcinspection.com/training/ to learn more about any of the methods in detail.

Visit our technical and career updates at our Blog site https://advancedqualitycentre.blogspot.com . or

https://ndtcenter.blogspot.com

Location: Advanced Quality Centre,116-B, 5th St Ext, near Kalyan Jewellers, 5th Street Extension, Doctor's Colony, Gandhipuram, Tamil Nadu 641012, India

Comments

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more