Welding inspection Methods

 Welding is a process of joining metals by process of heating.  Most of the weld made are manual. It is possible that the weld may have various defect formation due to parameters of welding and poor workmanship.



Why is Welding Inspection Methods  important?

Therefore the weld made should be tested for defects and quality of weld metal. To ensure the joint is strong and suitable for the purpose the product is designed for.

The Welding inspection methods can be broadly divided into two types

  • Destructive Testing and
  • Non Destructive Testing

 

Destructive Testing otherwise called as Mechanical Testing. It is a qualitative analysis process, which identifies the qualities like Tensile Strength, % of elongation, Hardness, Toughness, Chemical Content of metal and Micro Structure formed during welding process.

But destructive testing cannot be done on all the weld joints made. Instead it is carried out on a sample per lot. Mostly the above mentioned destructive testings are carried out to qualify a welding procedure or to qualify a welder .

Non Destructive Testing, or simply NDT is a quantitative analysis process. It identifies the presence of defects and sometimes used to measure the dimensions .

Welding Inspection

Basic NDT Methods on Weld Joints

There are various NDT Methods that can be applied on weld joints, few of them are mentioned below:

  • Ultrasonic Testing ( UT )
  • Phased Array Ultrasonic Testing ( PAUT )
  • Time of Flight Diffraction ( TOFD )
  • Radiography Testing ( RT )
  • Magnetic Particle Testing ( MT )
  • Liquid Penetrant Testing ( PT )
  • Laser Shearography
  • Microwave Testing (used on high density polyethylene weld joints)
  • Positive Material Identification PMI (used for Chemical analysis of welds & metals)
  • Acoustic Emission Testing ( AE )
  • Thermography

And much more…………..

The most widely used method for weld inspection are UT, PT, RT ,MT and VT

How to run a fabrication company making quality welds ?

It is essential for a successful fabrication company to have a welding procedure for each kind of welding.  Having a WPS (Welding Procedure Specification) is also requirement of Standards and Codes.

What is welder certificate?

The Welder performing the job should be skilled. Welder should be tested to perform the job and certified with a welder qualification certificate as per the codes or standards requirement.

What is the use of welder certification?

The Quality team should be with education of Weld Visual defects and inspection methods.

A suitable non destructive Testing method should be implemented to check the weld quality, randomly or 100% percentage , as per the client requirement.

Trainings for welders, trainings for Welding inspections, Courses and Certification for performing  NDT, consultancies for welding procedure Specification WPS , Welder qualification in Coimbatore etc., are readily available globally everywhere, for more assistance contact experts at https://aqcinspection.com/ .

Visit our technical and career updates at our Blog site https://advancedqualitycentre.blogspot.com . https://ndtcenter.blogspot.com our website https://aqcinspection.com/news-events/  for many more blogs

Location: 116-B, 5th St Ext, 5th Street Extension, Gandhipuram, Tamil Nadu 641012, India

Comments

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more