Why is X ray or radiography testing RT done in industries?

The metallic or non-metallic components manufactured in industries are possibly having various inherent defects few of which are mentioned below:
Casting Defects:– Blow holes, Shrinkage, Porosity, Pipes, Inclusions, Cold shut, Mis-run, Hot tears, segregation. To know more in detail about the causes and types of defects click https://aqcinspection.com/ndt-for-castings/ 
Welding Defects:– Undercut, Under fill, Lack of fusion , Lack of Penetration, Excess Penetration, Root Concavity of Suck back, Slag Inclusion, Improper weld bead, Overlap, Crater Pipe, Crater Cracks, HAZ Cracks, Weld Longitudinal or transverse crack, Spatters, Arc Strikes and much more. To know more about the causes & identification of defects click https://aqcinspection.com/welding-inspection-ndt-services/
These defects have to be identified in the initial stages to avoid major loss to the company, by avoiding processing cost losses. So X ray or Radiography Testing done in industries.
The discontinuities inside the components ( Castings, Forgings, extrusions and  Weld Joints) can be identified and visually captured using Radiographic Inspection or X ray Inspection techniques.

What is X Ray or Gamma  Radiography  Testing?

Radiography is the technique of graphing an image using Radiations, the electromagnetic radiations are used for these purposes.

What is electromagnetic Radiation?

Electromagnetic radiations are radiations carrying both electric & magnetic field with it; both fields in perpendicular direction to each other. Examples of these radiations are Heat radiation, Light Radiation, etc., only difference between them and X ray is their wavelength or frequency.
X ray or Gamma Radiation has higher frequency than visible light or heat radiation.
These high frequency radiations can penetrate through matters and also can form image on photosensitive films and electronic sensors, thus formed images are viewed to find out internal defects.

What is difference between X Ray and Gamma Ray ?

X rays and Gamma Ray differs by their source of emitter.
X rays are electromagnetic radiation emitted form an Electric device called X ray tube head, and it can be ON/OFF using switches, even their intensities are controlled by Voltage and current regulators.
Gamma Ƴ-Rays  are electromagnetic radiations emitted for radio-decaying isotopes , it cannot be ON/OFF , instead it can be only concealed in an enclosure, its energy or intensity is constant and depends upon the decaying source strength, only the time of radiation exposure can be controlled by bringing the source out of enclosure.

What is Isotopes?

Isotopes are elements having same atomic number but different mass number, for simple explanation read below:
An element is always determined by it atomic number, i.e. number of protons inside its atom (example: Carbon has 6 Protons, Oxygen has 8 protons), but the number of neutrons inside the atom can vary, thus the atoms having different number of neutrons are said to have different mass number and are called isotopes of that element.

What are Radio Active Isotopes?

The Elements having Equal number of protons and neutrons inside its atom is stable. But when the equation varies to an extent the atom become unstable and starts emitting energy in form of radiation to make the number of protons and neutrons equally stable inside the nucleus, these isotopes are called as Radio Active Isotopes.

What is Photo Sensitive Film ?

Photo Sensitive films are films manufactured to be reactive to electromagnetic radiations such as light, heat and x ray or gamma radiation.
They consist of Silver Halides such as Silver Bromides which chemically reacts when touches light or radiation, thus it captures data’s in form of reacted salts, It forms actual image when it undergoes processing called developing.
To Know more about X ray or Radiography Testing RT visit my webpage https://aqcinspection.com/news-events/ , call us for NDT Inspection Services such as Ultrasonic Testing, Liquid Penetrant testing , MPI Inspection, Welder Qualification. Visit our blogsite to know about our updates are NDT services and ndt inspection at https://advancedqualitycentre.blogspot.com/ or https://ndtcenter.blogspot.com/

Comments

Post a Comment

Popular posts from this blog

Discontinuities in Ultrasonic Testing in NDT

Image
 This blog will discuss types of discontinuities that can be evaluated with the ultrasonic testing in NDT method. Discontinuities can be divided into three general categories inherent, processing and service Inherent discontinuities are usually formed when the metal is molten. Inherent wrought discontinuities relate to the melting and solidification of the original ingot before it is formed into slabs, blooms and billets. Inherent cast discontinuities relates to the melting, casting and solidification of a cast article. Usually caused by inherent variables such as inadequate feeding, gating, excessive pouring temperature or entrapped gases. Processing discontinuities are usually related to the various manufacturing process such as machining, forming, extruding, rolling, welding, heat treating and plating. Service discontinuities are related to the various service conditions such as stress, corrosion, fatigue and erosion. During the manufacturing process, many disco
Read more

NDT on Shafts

Image
  Non Destructive Testing,NDT on Shafts is considered essential , because the shafts are mostly made as load bearing structures, any defects such as cracks will propagate more during acting of load and eventually will cause failure. The most possible defects in shafts are Cracks and Pipes , which is shown below The Non Destructive methods preferred for defect detection on raw material shafts are Ultrasonic Testing, Magnetic Particle testing / Eddy Current Testing / Magnetic Flux Leakage method. We have not discussed about other NDT methods such as Liquid Penetrant testing & Radiographic testing because for raw material inspection. These methods will be cost effective for raw material testing  ( i.e. most costly and labor intensive, also there is possibility of missing out the cracks in radiography testing due to orientation of crack ) The Defect wise identification method is given as below  , Internal Defect ( Piping ) – Ultrasonic Testing Surface Defects  (C racks) – Magnetic Part
Read more

Standards for Welding Positions

Image
  Standards for Welding Positions : It is very important for the Weld Inspector  to know the position , or location of a joint relative to the horizon, because it may determine what welding process, methods, and techniques can be used. Welding is usually easiest when the welder can work on a joint located on a flat, horizontal surface, such as on a table or bench. However, joints in the field may be located in a variety of positions relative to the welder and to the horizon, as shown below.  1)  Welding positions – AWS D1.1, European Welding Standard EN 287 – 1, ASME IX: 2) Welding Positions – Butt, Fillet and Piping Welds: Flat Butt Weld Position – 1G In this position, the axis line of the weld must  not incline more than 15°  from the horizon and the face of the weld must be on top. Welders often refer to the flat-position welding by the nonstandard term  downhand welding. Horizontal Butt Weld Position – 2G In this position, both plates are perpendicular to the bench top, but the axi
Read more